This table represents a segment of Permabond’s complete line of structural acrylic adhesives. Contact a technical representative at Permabond to discuss your specific application requirements. We will be able to recommend the most suitable adhesive for your application.
Grade (Click grade number for TDS) | Description | Viscosity mPa.s (cP) | Fixture Time | Shear Strength MPa (psi) | Availability |
---|---|---|---|---|---|
TA430 | Very high strength bonding of metals, plastics, ceramics and wood. Fast cure on close fitting parts. | 20rpm: 20,000 2.5rpm: 50,000 | 1-2 mins (no gap) | 15 - 25 (2,200 - 3,600) | Worldwide |
TA435 | Very high strength bonding of metals, ferrites and thermoplastics. High impact applications. | 20rpm: 30,000 2.5rpm: 70,000 | 1-2 mins (no gap) | 15 - 25 (2,200 - 3,600) | Worldwide |
TA436 | Very high strength bonding of metals, ferrites and hard plastics. High impact and high temperature applications. | 20rpm: 25,000 2.5rpm: 60,000 | 20-30 secs (no gap) | 15 - 25 (2,200 - 3,600) | Worldwide |
TA437 | Single component. To bond ferrites and metals. For high temperature applications. Initiator 41 will accelerate cure. | 20rpm: 40,000 2.5rpm: 130,000 | 5-10 mins (20-30 secs with Initiator 41) | 14 - 20 (2,000 - 3,000) | Worldwide |
TA439 | Methacrylic acid free structural adhesive for magnet bonding. Ideal for sealed electric motors. High temperature resistance. | 20 rpm: 1,000 | 20-40 secs | 20 - 25 (2,900 – 3,600) | Worldwide |
TA440 | Bead on bead for rapid bonding of metal, glass, wood and rigid plastics. | Mixed: 10,000 | 15-30 secs | 15 - 25 (2,200 - 3,600) | Worldwide |
TA452 | Low odour, for structural bonding of metals. Non-flammable - easy to transport and store. | 20rpm: Mixed: 4,500 | 6-9 mins | 28-32 (4060-4640) | Worldwide |
TA4522 | Low odour, for bonding plastics. Non-flammable - easy to transport and store. | Mixed: 4,500 | 10-15 mins | 21-23 (3045-3335) | Worldwide |
TA459 | Methacrylic acid free structural adhesive for magnet bonding. Non-corrosive, ideal for sealed electric motors. | 20rpm: 20,000 2.5rpm: 80,000 | 20-40 secs | 20 - 25 (2900 - 3600) | Worldwide |
TA4200 | 2-part 1:1 rapid curing, gap filling, toughened. Ideal for structural bonding of aluminium. | Mixed: 45,000 | 7-10 mins | 23-25 (3,300-3,600) | Europe |
TA4202 | 2-part 1:1 pink / green acrylic with ultra-high peel strength. Ideal for structural bonding of aluminium. | Mixed: 4,000 | 2-3 mins | 24-25 (3,500-3,600) | Europe |
TA4204 | 2-part 1:1 crystal clear acrylic for bonding plastics. | Mixed: 55,000 | 1-2 mins | PMMA: 4-5 (580-725) | Europe |
TA4210 | 2-part 1:1 longer handling time than TA4200, gap filling, toughened. Ideal for structural bonding of aluminium. | Mixed: 45,000 | 20-25 mins | 23-25 (3,300 – 3,600) | Europe |
TA4246 | No-mix resin and initiator for high strength bonding of metal, glass, composites and plastics. | 20rpm: 28,000 | 1-2 mins | 33 - 35 (4,800 - 5,100) | Worldwide |
TA4590 | Methacrylic acid free structural adhesive for magnet bonding. Non-corrosive, ideal for sealed electric motors. High viscosity. | 20rpm: 20,000 2.5rpm: 90,000 | 15-30 secs | 20 - 25 (2,900 – 3,600) | Worldwide |
TA4605 | Mixed: 125,000 | 5-10 mins | Polyprop: 5-8 (725-1200) | Worldwide | |
TA4610 | 2-part 1:1. For bonding untreated polyolefins (such as polypropylene and polyethylene. | Mixed: 210,000 | 12-15 mins | Polyprop: 5-8 (725-1200) | Worldwide |
TA4611 | 2-part 1:1. For bonding untreated polyolefins (such as polypropylene and polyethylene. | Mixed: 18,500 | 10-16 mins | Polyprop: 4-6 (580-870) | Worldwide |
TA4631 | 2-part 1:1 PP/PE bonder, no odour | Mixed: 21,500 | 12-18 mins | Polyprop: >8 N/mm² (>1200 psi) | Worldwide |
TA4810 | 2-part 1:1 develops strength rapidly. Toughened, ideal for structural bonding of plastics & unprimed metals. | Mixed: 135,000 - 215,000 | 10-15 mins | 21 - 28 (3,000 – 4,000) | Americas |
TA4820 | 2-part 1:1 longer handling time than TA4810. Toughened, ideal for structural bonding of plastics & unprimed metals. | Mixed: 160,000-250,000 | 30-35 mins | 21 - 28 (3,000 – 4,000) | Americas |