Permabond Structural Acrylic Adhesives Product Selector
This table represents a segment of Permabond's complete line of structural acrylic adhesives. Contact a technical representative at Permabond to discuss your specific application requirements. We will be able to recommend the most suitable adhesive for your application.
Contact us for more information
|
Grade (Click grade number for TDS) |
Description |
Mixed Viscosity (mPa.s) cP |
Handling Time |
Shear Strength MPa (psi) |
Availability |
|
Very
high strength bonding of metals, plastics, ceramics and wood. Fast cure on
close fitting parts. |
28,000
- 32,000 |
2-20 mins (depending on
gap) |
15
- 25 (2,200
- 3,600) |
Worldwide |
|
|
Very
high strength bonding of metals, ferrites and thermoplastics. High impact
applications. |
85,000
- 95,000 |
2-20 mins (depending on
gap) |
15
- 25 (2,200
- 3,600) |
Worldwide |
|
|
Very
high strength bonding of metals, ferrites and hard plastics. High impact and
high temperature applications. |
16,000
- 18,000 |
1-3
mins |
15
- 25 (2,200
- 3,600) |
Worldwide |
|
|
Single
component. To bond ferrites and metals. For high temperature applications. Initiator
41 will accelerate cure. |
115,000
- 125,000 |
3-5
mins |
14
- 20 (2,000
- 3,000) |
Worldwide |
|
|
Methacrylic
acid free structural adhesive for magnet bonding. Ideal for sealed electric
motors. High temperature resistance. |
800
- 1,200 |
|
20
- 25 (2900
- 3600) |
Worldwide |
|
|
2-part
1:1 longer handling time than TA4300, gap filling, toughened. Ideal for
structural bonding of aluminium. |
Paste |
10-15
mins |
24
- 26 (3500
- 3800) |
|
|
|
Methacrylic acid free structural adhesive for magnet bonding. Non-corrosive, ideal for sealed electric motors. Maximum gap fill. |
10,000-30,000 |
15-30 seconds |
20
- 25
(2900
- 3600)
|
Worldwide |
|
|
Bead
on bead for rapid bonding of metal, glass, wood and rigid plastics. |
8,000-12,000 |
<30
seconds |
15
- 25 (2,200
- 3,600) |
Worldwide |
|
|
No-mix
resin and initiator for high strength bonding of metal, glass, composites and
plastics. |
28,000
- 32,000 |
2-4
mins |
35
- 35 (4,800
- 5,000) |
|
|
|
2-part
1:1 rapid curing, gap filling, toughened. Ideal for structural bonding of
aluminium. |
Paste |
5-10
mins |
20
- 22 (2900
- 3200) |
|
|
|
2-part
1:1 very rapid cure, can be applied bead on bead,
multipurpose. |
4,000
- 5,000 |
3-5
mins |
22
- 25 (3200
- 3600) |
|
|
|
2-part 1:1 develops strength rapidly. Toughened, ideal for structural bonding of plastics & unprimed metals. |
90,000 to 100,000 |
10-15 mins |
20
- 31 (3000
- 4500) |
|
|
|
2-part 1:1 longer handling time than TA4810. Toughened, ideal for structural bonding of plastics & unprimed metals. |
90,000 to 100,000 |
30-35 mins |
20
- 31 (3000
- 4500) |
|